モデル: A-3070/B-8280
ブランド: Xuchuan Chemical
原産地: 中国
の種類: 合成樹脂とプラスチック
Application: Industrial tyre wheel
Product Name: Polyurethane
Characteristic: Good handle, smooth surface
Appearance: liquid
Code: A-3070/B-8280
Package(kg): 18/20
PUホイール化学物質
フォームタイヤ用のPUレジンポリウレタンポリオールISO
ホイールポリウレタン鋳造樹脂
Application | Industrial tyre wheel |
Product name | Polyurethane |
A/B Materials Temperatures(℃) | 40~45/38~42 |
A+C/B Mix ratio (By weight) | 100/101~103 |
Cream Time (s) | 8~10 |
End of Rise Time (s) | 60~70 |
Free Rise Foam Density(g/cm3) | 0.24~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | 5~7 |
Characteristic: Good handle, smooth surface |
|||||||
Application: Tire |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
||
A-3070 |
Liquid |
1000~1400 |
1.01~1.02 |
18 |
|||
B-8280 |
Yellowish transparent liquid or waxy |
800~1200 |
1.08~1.2 |
20 |
|||
Materials preheat |
|||||||
A-3070: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-8280: preheated at 50~60℃ for 10~12 hours. |
|||||||
Typical processing parameters & Reaction parameter |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/101~103 |
8~10 |
60~70 |
0.24~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 250g±10g/18kg |
|||||||
The adding content of water should be 0~90g/18kg according to the reality |
|||||||
The adding content of hardener should be 0~600g/18kg according to the reality |
|||||||
Physical properties |
|||||||
Items |
Molded Density |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
|
|
|
|
||||||
Physical properties |
0.50~0.70 |
55~68 |
7.5~9.0 |
340~450 |
24~33 |
|
|
Demold time may be prolonged with the increase of sole thickness. |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.