モデル: XC-9080W/XC-6088W
ブランド: Xuchuan
原産地: 中国
の種類: 合成樹脂とプラスチック
Chemical: PU
Keywords: flexible polyurethane resin
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Application: Outsole, slippers, wedge shoes
Code: XC-9080W/XC-6088W
Brand: XUCHUAN
製品説明
低密度と高い硬度、良好な外観、リトルピンホール、および弱いフォームライン
Application | shoe sole |
Keywords | flexible polyurethane resin |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
Demold time may be prolonged with the increase of sole thickness. |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
PUハードマテリアル
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.